Welcome Alloy 6060

17th December 2015

Welcome Alloy 6060

Alloy 6060 has a strength slightly lower than 6005A. It has very good weldability and very good plus corrosion resistance. This alloy is commonly used for complex cross sections and also has a very good anodizing response. Applications for alloy 6060: Interior sections, architectural sections, frame systems, fences, railings, ladder, furniture, office equipment, electronic modules.

Alloy	Chemicial Composition								Other	Other	Al.
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Each	Total	Min
6060	0.30 to 0.60	0.10 to 0.30	0.10 max	0.10 max	0.35 to 0.60	0.05 max	0.15 max	0.10 max	0.05 max	0.15 max	Residual

Mechanical Properties

Alloy	Temper	Thickness		Tensile Strength (MPA)		Proof Stress (MPA)		Elongation %	Hardness
Alloy	Temper	Over	Up to	Min	Max	Min	Max	Elongation %	Webster	Rockwell E
6060 or 6063	T4	All Thickness		130	–	70	–	14 min	4 – 7	41 – 54
	T5	All Thickness		150	–	110	–	8 min	8 min	55 min
	T52	All Thickness		150	205	110	170	8 min	8- 11	55 – 70
	T6	All Thickness		205	–	170	–	8 min	8 min	70 min

News Uncategorized

17th December 2015

Welcome Alloy 6101

Admin Interbrucke

Aluminium / Aluminum 6101 alloy has good mechanical strength and high electrical conductivity.
The following datasheet will discuss in detail about Aluminium / Aluminum 6101 alloy.

Alloy	Chemicial Composition								Other	Other	Al.
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Each	Total	Min
6101	0.30 to 0.70	0.50 max	0.10 max	0.03 max	0.35 to 0.80	0.03 max	0.10 max	0.10 max	0.05 max	0.15 max	Residual

Mechanical Properties

Alloy	Temper	Thickness		Tensile Strength (MPA)		Proof Stress (MPA)		Elongation %	Hardness
Alloy	Temper	Over	Up to	Min	Max	Min	Max	Elongation %	Webster	Rockwell E
6061	T4	All Thickness		180	–	110	–	16 min	8 min	62 min
6061	T6	All Thickness		260	–	240	–	8 min	15 min	89 min

News Uncategorized

17th December 2015

Welcome Alloy 6005A

Admin Interbrucke

Aluminium alloy 6005A is a medium strength alloy. It’s heat treatable with excellent corrosion resistance. Alloy 6005A can sometimes be used interchangeably with alloy 6061, 6005A though has better extrusion characteristics and a better mill surface finish. It is difficult to produce thin-wall or complicated extrusions in 6005. 6005A tube has very good bending properties.
Applications 6005 and 6005A can be used for furniture, ladders, bus profile structures and other profiles which need greater strength compare to what given by alloy 6063

Alloy	Chemicial Composition								Other	Other	Al.
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Each	Total	Min
6005A	0.50 to 0.90	0.35 max	0.30 max	0.06 to 0.25	0.40 to 0.70	0.06 to 0.25	0.20 max	0.10 max	0.05 max	0.15 max	Residual

Mechanical Properties

Alloy	Temper	Thickness		Tensile Strength (MPA)		Proof Stress (MPA)		Elongation %	Hardness
Alloy	Temper	Over	Up to	Min	Max	Min	Max	Elongation %	Webster	Rockwell E
6005 or 6005A	T4	All Thickness		170	–	100	–	16 min	8 min	54 min
	T5	All Thickness		260	–	240	–	8 min	15 min	90 min
	T6	All Thickness		260	–	240	–	8 min	15 min	90 min